Alloy 321 (UNS S32100) is a titanium stabilized austenitic stainless steel with good general corrosion resistance. It has excellent resistance to intergranular corrosion after exposure to temperatures in the chromium carbide precipitation range of 800 – 1500°F (427 – 816°C). The alloy resists oxidation to 1500°F (816°C) and has higher creep and stress rupture properties than alloys 304 and 304L. It also possesses good low temperature toughness.
Alloy 321H (UNS S 32109) is the higher carbon (0.04 – 0.10) version of the alloy. It was developed for enhanced creep resistance and for higher strength at temperatures above 1000oF (537°C). In most instances, the carbon content of the plate enables dual certification.
Used in Food Industries, Chemical Industries , Electrielcal Industries, Genrater Industries, Shaft Industries, Cement Industries, Gas Industries, Power Project etc..
| Standard | : | ASTM A240 / ASME SA240 |
| Thickness of Coils | : | Ranging from 0.3mm to 10mm |
| Thickness of Sheets (Cold Rolled) | : | Ranging from 0.3 mm to 6 mm |
| Thickness of Sheets / Plates (Hot Rolled) | : | Ranging from 3.0 mm to 20 mm |
| Width | : | 1000mm / 1219mm /1250mm / 1500mm / 2000mm | Hardness | : | As per ASME A & NACE MR 175 |
| Finish | : | Hot rolled plate (HR), Cold rolled sheet (CR), 2B, 2D, BA NO(8), SATIN (Met with Plastic Coated) |
| Form | : | Coils, Foils, Rolls, Plain Sheet, Shim Sheet, Perforated Sheet, Chequered Plate, Strip, Flats, Blank (Circle), Ring (Flange) etc. |
| % | Cr | Ni | C | Si | Mn | P | S | N | Ti | Fe |
|---|---|---|---|---|---|---|---|---|---|---|
| 321 | min:17.0 max:19.0 |
min: 9.0 max:12.0 |
max:0.08 | max:0.75 | max:2.0 | max:0.045 | max:0.03 | max:0.10 | min:5*(C+N) max:0.70 |
Balance |
| 321H | min:17.0 max:19.0 |
min: 9.0 max:12.0 |
min:0.04 max:0.10 |
min:18.0 max:20.0 |
max:2.0 | max:0.045 | max:0.03 | max:0.10 | min:5*(C+N) max:0.70 |
Balance |
| Denstiy lbm/in3 |
Coefficient of Thermal Expansion (min/in)-°F |
Thermal Conductivity BTU/hr-ft-°F | Specific Heat BTU/lbm -°F | Modules of Elasticity (annealed)2-psi | |
|---|---|---|---|---|---|
| at 68 °F | at 68 – 212°F | at 68 – 1832°F | at 200°F | at 32 – 212°F | in tension (E) |
| 0.286 | 9.2 | 20.5 | 9.3 | 0.12 | 28 x 106 |