NG Industries are manufacturers, exporters & suppliers of 316/316H Stainless Steel Plates. We are occupied with offering a wide and wonderful scope of 316/316H Stainless Steel Plates. Made utilizing subjective stainless steel, these plates are offered by us in changed measurements, evaluations and sizes. Attributable to the non-destructive nature and strength, every one of our items are widely utilized as a part of development works. Further, we guarantee that exclusive immaculate Stainless Steel 316/316H Stainless Steel Sheet are conveyed at supporters' premises inside the planned time.
Alloy 316/316H is molybdenum-bearing austenitic stainless steel. The higher nickel and molybdenum content in this grade allows it to demonstrate better overall corrosion resistant properties than 304, especially with regard to pitting and crevice corrosion in chloride environments. In addition, Alloy 316/ 316H provides excellent elevated temperature tensile, creep and stress-rupture strengths, as well as outstanding formability and weldability. 316L is the lower carbon version of 316 and is immune from sensitization; therefore, it is very frequently used in heavy gauge welded components.
| Standard | : | ASTM A240 / ASME SA240 |
| Thickness of Coils | : | Ranging from 0.3mm to 10mm |
| Thickness of Sheets (Cold Rolled) | : | Ranging from 0.3 mm to 6 mm |
| Thickness of Sheets / Plates (Hot Rolled) | : | Ranging from 3.0 mm to 20 mm |
| Width | : | 1000mm / 1219mm /1250mm / 1500mm / 2000mm |
| Length | : | 2000 mm / 2440 mm / 2500 mm / 3000 mm / 6000 mm | Hardness | : | As per ASME A & NACE MR 175 |
| Finish | : | Hot rolled plate (HR), Cold rolled sheet (CR), 2B, 2D, BA NO(8), SATIN (Met with Plastic Coated) |
| Form | : | Coils, Foils, Rolls, Plain Sheet, Shim Sheet, Perforated Sheet, Chequered Plate, Strip, Flats, Blank (Circle), Ring (Flange) etc. |
| C | Mn | Si | P | S | Cr | Mo | Ni | N | |
|---|---|---|---|---|---|---|---|---|---|
| 316 (S31600) |
0.08 max |
2.0 max |
0.75 max |
0.045 max |
0.03 max |
min: 16.0 max: 18.0 |
min: 2.0 max: 3.0 |
min: 10.0 max: 14.0 |
0.10 max |
| 316L (S31603) |
0.03 max |
2.0 max |
0.75 max |
0.045 max |
0.03 max |
min: 16.0 max: 18.0 |
min: 2.0 max: 3.0 |
min: 10.0 max: 14.0 |
0.10 max |
| Grade | Tensile Strength ksi (min) |
Yield Strength 0.2% ksi (min) |
Elongation % | Hardness (Brinell) MAX | Hardness (Rockwell B) MAX |
|---|---|---|---|---|---|
| 316 (S31600) |
75 | 30 | 40 | 217 | 95 |
| 316L (S31603) |
70 | 25 | 40 | 217 | 95 |
| Density lbm/in3 |
Thermal Conductivity (BTU/h ft. °F) |
Electrical Resistivity (in x 10-6) |
Modulus of Elasticity (psi x 106 |
Coefficient of Thermal Expansion (in/in)/°F x 10-6 |
Specific Heat (BTU/lb/°F) |
Melting Range (°F) |
|---|---|---|---|---|---|---|
| 0.29 at 68°F | 100.8 at 68 212°F | 29.1 at 68°F | 29 | 8.9 at 32 – 212°F | 0.108 at 68°F | 2500 to 2550 |
| 9.7 at 32 – 1000°F | 0.116 at 200°F | |||||
| 11.1 at 32 – 1500°F |