Stainless steel 410 is the basic, general purpose martensitic stainless steel that is used for highly stressed parts and provides good corrosion resistance plus high strength and hardness. Alloy 410 contains a minimum of 11.5% chromium which is just sufficient enough to demonstrate corrosion resistance properties in mild atmospheres, steam, and many mild chemical environments. It is a general purpose grade that is often supplied in the hardened but still machineable condition for applications where high strength and moderate heat and corrosion resistance are required. Alloy 410 displays maximum corrosion resistance when it’s been hardened, tempered, and then polished.
Our firm has marked in the industry for Stainless Steel Coil 410. These products are widely employed in the market for their durability. Our presented product is manufactured as per universal industry norms employing the top quality raw material, sourced from dependable sellers of market. Owing to easy to use, these products are widely employed in the industry.
We supply 410 stainless steel sheet in a variety of lengths and widths and can custom cut to your exact specifications. 409 coil can also be slit to your desired width.
Used in Food Industries, Chemical Industries , Electrielcal Industries, Genrater Industries, Shaft Industries, Cement Industries, Gas Industries, Power Project etc..
| Standard | : | ASTM A240 / ASME SA240 |
| Thickness of Coils | : | Ranging from 0.3mm to 10mm |
| Thickness of Sheets (Cold Rolled) | : | Ranging from 0.3 mm to 6 mm |
| Thickness of Sheets / Plates (Hot Rolled) | : | Ranging from 3.0 mm to 20 mm |
| Width | : | 1000mm / 1219mm /1250mm / 1500mm / 2000mm | Hardness | : | As per ASME A & NACE MR 175 |
| Finish | : | Hot rolled plate (HR), Cold rolled sheet (CR), 2B, 2D, BA NO(8), SATIN (Met with Plastic Coated) |
| Form | : | Coils, Foils, Rolls, Plain Sheet, Shim Sheet, Perforated Sheet, Chequered Plate, Strip, Flats, Blank (Circle), Ring (Flange) etc. |
| C | Mn | Si | P | S | Cr | Ni | |
|---|---|---|---|---|---|---|---|
| 410 | 0.15 max | 1.00 max | 1.00 max | 0.04 max | 0.03 max | min: 11.5 max: 13.5 |
0.50 max |
| Grade | Tensile Strength ksi (MPa) min | Yield Strength 0.2% offset ksi (MPa) min | Elongation (% in 50mm) min | Hardness (Brinell) MAX | Hardness (Rockwell B) MAX |
|---|---|---|---|---|---|
| 410 | 65 (450) | 30 (205) | 20 | 217 | 96 |
| Heat Treatment | T410 (0.14%C) Hardened 1800°F (982°C) | ||
|---|---|---|---|
| Rockwell Hardness | 0.2% YS, Ksi (MPa) | UTS, Ksi (MPa) | |
| Annealed* | 81 HRB | 45.4 (313) | 80.4 (554) |
| Hardened & Tempered 400°F (204°C) | 43 HRC | 156.1 (1076) | 202.9 (1399) |
| Hardened & Tempered 550°F (288°C) | 40 HRC | 148.3 (1022) | 187.0 (1289) |
| Hardened & Tempered 600°F (316°C) | 40 HRC | 148.8 (1026) | 186.1 (1283) |
| Hardened & Tempered 800°F (427°C) | 41 HRC | 132.9 (916) | 188.5 (1300) |
| Hardened & Tempered 900°F (482°C) | 41 HRC | 122.6 (845) | 154.3 (1063) |
| Hardened & Tempered 1000°F (538°C) | 35 HRC | 127.9 (882) | 154.3 (1063) |
| Hardened & Tempered 1200°F (649°C) | 98 HRB | 85.5 (589) | 111.2 (767) |